Only by applying a perfect polish, jewelery gets their appealing appearance. On one side the abrasiveness should be as low as possible to avoid material loss and on the other side high luster without any microcracks is targeted. The abrasive material plays an important role to achieve these targets.

ULTIMATE-Series

ULTIMATE P 815

Special polishing alumina with top cut of 45µm and high oil absorption for finishing of soft metals, plastics and paints.

ULTIMATE P 1500

Special polishing alumina with tight particle size distribution and a top cut of 45µm achieving very high cut on plastics and paints.

ULTIMATE P 2500

Special polishing alumina with a very tight controlled top cut of <20µm for high end finishing applications.

P-Series

P 2

Alumina with top cut of 90 µm produced in Germany. The "workhorse" in polishing industry giving high cut and good polish in on go.

P 2 FR

Alumina with top cut of 90 µm and fines removed. Due to removal of fine fraction the material has a high loose bulk density and oil absorption

P 730

Alumina with top cut of 56 µm for the finishing of all kinds of surfaces.

P 10 feinst

Alumina with top cut of 20 µm giving nearly scratch free surfaces.

P 30

Alumina with top cut of 90 µm for the finishing of all kinds of surfaces

RAPOL-Series

RAPOL 100

Alumina with SSA of 4 m²/g and  top cut of 200 µm for high cutting compounds.

RAPOL 500

Ground Alumina with SSA of 4,5 m²/g top cut of 90 µm. Further development of products like P2 and P2 FR for higher cut and similar polishing results.

RAPOL 140

Alumina with SSA of 4 m²/g and  top cut of 90 µm for high cutting compounds.

RAPOL 600

Ground Alumina with SSA of 5 m²/g top cut of 63µm.

RAPOL 900

Ground Alumina with SSA of 6 m²/g top cut of 45µm µm.